Deskrizzjoni tal-Prodott
ASTM standard 7020 aluminju liga bar/virga
Ippakkjar u Kunsinna
dettall tal-ippakkjar: pakkett standard tal-esportazzjoni, bħala l-ħtieġa tiegħek
Dettall tal-kunsinna: Mibgħut fi 15-il jum wara l-ħlas
Introduzzjoni tal-prodott
| Speċifikazzjoni | |||
| 1. | isem tal-komodità | ASTM standard 7020 aluminju liga bar/virga | |
| 2. | Standard | ASTM B221M, GB/T 3191, JIS H4040, eċċ. | |
| 3. | Materjal | 7005,7020,7022,7050,7075,7475, 2014,2014A,2214,2017,2017A,2117 5086, 5056,5456, 2024, 2014, 6061, 6063,6082, eċċ. |
|
| 4. | Speċifikazzjonijiet | Dijametru | 2-800mm |
| Tul | 2m, 3m, 5.8m, 6m, jew kif meħtieġ | ||
| 5. | Wiċċ | Finitura tal-mitħna, illustrata, anodizzar, tfarfir, blasting tar-ramel, kisi tat-trab, eċċ | |
| 6. | MOQ | 500kg | |
| 7. | Terminu tal-Prezz | Ex-xogħol, FOB, CIF , CFR, eċċ. | |
| 8. | Terminu ta' Ħlas | T/T, L/C, eċċ. | |
| 9. | Ħin ta' Kunsinna | Skont il-kwantità tal-ordni. | |
| 10 | Esportazzjoni lejn | Singapor, Indoneżja, Ukraina, Korea, Tajlandja, Vjetnam, Għarabja Sawdija, Brażil, Spanja, Kanada, USA, Eġittu, Iran, Indja, Kuwajt, Dubai, Oman, Il-Kuwajt, il-Perù, il-Messiku, l-Iraq, ir-Russja, il-Malasja, eċċ. |
|
| 11. | Pakkett | Pakkett standard ta 'esportazzjoni: kaxxa tal-injam magħquda, libsa għal kull tip ta' trasport, jew tkun meħtieġa. |
|
| 12. | Applikazzjoni | 1) Tagħmir tal-kċina, ikel u prodotti kimiċi għall-ipproċessar u l-ħażna; 2) Tankijiet tal-karburant tal-ajruplani, pajp taż-żejt, rivets, wajer; 3) Kopertura tal-bottijiet, pannelli tal-karrozzerija tal-karozzi, pjanċi tal-istering, stiffeners, parentesi u komponenti oħra; 4) Manifattura ta 'trakkijiet, bini ta' torri, vapur, ferrovija, għamara, partijiet tal-makkinarju, preċiżjoni makkinar mal-tubi, vireg, iffurmat, folja tal-metall. |
|
| 13. | Kuntatt | Jekk għandek xi mistoqsija, jekk jogħġbok tħossok liberu li tikkuntattjani. | |
Kompożizzjoni kimika
| Grad | Kompożizzjoni kimika | ||||||||||
| Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Ti | Zr | ||
| 7005 | 0.35 | 0.4 | 0.1 | 0.20~0.7 | 1.0~1.8 | - | 4.0~5.0 | - | 0.01~0.06 | 0.058~0.20 | - |
| 7020 | 0.35 | 0.4 | 0.2 | 0.05~0.50 | 1.0~1.4 | 0.10~0.35 | 4.0~5.0 | Zr + Ti: 0.08 ~ 0.25 | - | 0.08~0.20 | - |
| 7022 | 0.5 | 0.5 | 0.50~1.0 | 0.10~0.40 | 2.6~3.7 | 0.10~0.30 | 4.3~5.2 | Zr+Ti:0.20 | - | - | - |
| 7050 | 0.12 | 0.15 | 2.0~2.6 | 0.1 | 1.9~2.6 | 0.04 | 5.7~6.7 | - | 0.06 | 0.08~0.15 | - |
| 7075 | 0.4 | 0.5 | 1.2~2.0 | 0.3 | 2.1~2.9 | 0.18~0.28 | 5.1~6.1 | 0.2 | - | - | |
| 7475 | 0.1 | 0.12 | 1.2~1.9 | 0.06 | 1.9~2.6 | 0.18~0.25 | 5.2~6.2 | - | 0.06 | - | - |
Proprjetajiet Fiżiċi
| 7000 serje proprjetajiet fiżiċi tal-folja tal-liga tal-aluminju | |
| Saħħa tat-tensjoni | σb (MPa) Akbar minn jew ugwali għal 572 |
| Saħħa ta 'rendiment | σ0.2 (MPa) Akbar minn jew ugwali għal 503 |
| temper | T6,T651,T7451,H112 |
| Ebusija | HB150 |
| Titwil | >12 |
Kompożizzjoni kimika
| Grad | Kompożizzjoni kimika | ||||||||||
| Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Ti | Zr | ||
| 7005 | 0.35 | 0.4 | 0.1 | 0.20~0.7 | 1.0~1.8 | - | 4.0~5.0 | - | 0.01~0.06 | 0.058~0.20 | - |
| 7020 | 0.35 | 0.4 | 0.2 | 0.05~0.50 | 1.0~1.4 | 0.10~0.35 | 4.0~5.0 | Zr + Ti: 0.08 ~ 0.25 | - | 0.08~0.20 | - |
| 7022 | 0.5 | 0.5 | 0.50~1.0 | 0.10~0.40 | 2.6~3.7 | 0.10~0.30 | 4.3~5.2 | Zr+Ti:0.20 | - | - | - |
| 7050 | 0.12 | 0.15 | 2.0~2.6 | 0.1 | 1.9~2.6 | 0.04 | 5.7~6.7 | - | 0.06 | 0.08~0.15 | - |
| 7075 | 0.4 | 0.5 | 1.2~2.0 | 0.3 | 2.1~2.9 | 0.18~0.28 | 5.1~6.1 | 0.2 | - | - | |
| 7475 | 0.1 | 0.12 | 1.2~1.9 | 0.06 | 1.9~2.6 | 0.18~0.25 | 5.2~6.2 | - | 0.06 | - | - |
Proprjetajiet Fiżiċi
| 7000 serje proprjetajiet fiżiċi tal-folja tal-liga tal-aluminju | |
| Saħħa tat-tensjoni | σb (MPa) Akbar minn jew ugwali għal 572 |
| Saħħa ta 'rendiment | σ0.2 (MPa) Akbar minn jew ugwali għal 503 |
| temper | T6,T651,T7451,H112 |
| Ebusija | HB150 |
| Titwil | >12 |